Oxide-Scale Evolution on a New Ni–Fe-Based Superalloy at High Temperature

Oxidation of Metals - The isothermal oxidation behavior and oxide-scale evolution on a newly developed Ni–Fe-based superalloy were investigated. Three oxidation stages were generally...     

Enhanced relative permittivity in niobium and europium co-doped TiO2 ceramics

The appearance of colossal permittivity materials broadened the choice of materials for energy-storage applications. In this work, colossal permittivity in ceramics of TiO₂ co-doped with niobium and europium ions ((Eu_0.5Nb_0.5)_xTi_1-xO₂ ceramics) was reported. A large permittivity (ε_r ～ 2.01?×?10⁵) and a low dielectric loss (tanδ ～ 0.095) were observed for (Eu_0.5Nb_0.5)_xTi_1-xO₂ (x?=?1%) ceramics at 1?kHz. Moreover, two significant relaxations were observed in the temperature dependence of dielectric properties for (Eu, Nb) co-doped TiO₂ ceramics, which originated from defect dipoles and electron hopping, respectively. The low dielectric loss and high relative permittivity were ascribed to the electron-pinned defect-dipoles and electrons hopping. The (Eu_0.5Nb_0.5)_xTi_1-xO₂ ceramic with great colossal permittivity is one of the most promising candidates for high-energy density storage applications.     

退火工艺对激光选区熔化成形Ti6Al4V合金组织及室温力学性能的影响

以Ti6Al4V球形粉末为原料,利用激光选区熔化成形方法制备了Ti6Al4V合金试样,采用光学显微镜、扫描电镜及力学性能测试等手段,研究了退火工艺对Ti6Al4V合金室温力学性能及组织的影响规律。结果表明: SLM成形沉积态Ti6Al4V合金室温抗拉强度超过1200 MPa,而平均断后伸长率仅为4.0%;在650 ℃下进行真空退火处理,合金的抗拉强度仍保持在1200 MPa左右,规定塑性延伸强度R_p0.2高于1150 MPa,但试样的断后伸长率<10%;而在750及800 ℃下进行真空退火处理,合金试样的抗拉强度降至1100 MPa左右,规定塑性延伸强度高于1050 MPa,伸长率达到甚至超过10%,材料的综合强韧性得到明显提升。随着真空退火加热温度和保温时间的增加,SLM成形Ti6Al4V合金原始β晶界逐渐变模糊,晶粒趋向于等轴化。与此同时,快速冷却转变的α′针状马氏体未出现明显地粗化。     

Catalytic Hydrocracking of a Bitumen‐Derived Asphaltene over NiMo/γ‐Al2O3 at Various Temperatures

Hydrocracking of a bitumen‐derived asphaltene over NiMo/γ‐Al₂O₃ was investigated in a microbatch reactor at varying temperatures. The molar kinetics of asphaltene cracking reaction was examined by fitting the experimental data. Below a defined temperature, the molar reaction showed the first‐order kinetic feature while at higher temperatures secondary reactions such as coke formation became significant, causing deviation of the reaction behavior from the proposed first‐order kinetic model. Selectivity analysis proved that dominant products varied from gases to liquids to gases with increasing temperature, shifting the dominant reaction from C–S bonds cleavage to C–C bonds cleavage.     

Structures and properties of chicken myofibrillar protein gel induced by microwave heating

Structures and properties of myofibrillar protein gel prepared at different power (300–800 W) were evaluated. Amino acid analysis demonstrated that changes in microwave power did not alter primary structure of gel. However, an increase in microwave power could change higher structures of gel. As microwave power increased, α-helix content decreased and β-sheet content increased. Increased microwave power probably facilitated protein to unfold and expose the internal groups, causing surface hydrophobicity and the formation of disulphide bonds were enhanced, which indicated changes in tertiary and quaternary structures of protein. At 500 W, gel had the best ultrastructure where surface morphology, springiness and water holding capacity reached the optimum. Our findings suggested that microwave at an appropriate power (500 W) could change higher structures of myofibrillar protein gel to achieve desired processing and quality protein gel characteristics.     

强化研磨加工中喷射角度对GCr15轴承钢板塑性变形的影响

利用ABAQUS有限元仿真软件研究不同喷射角度强化研磨加工GCr15轴承钢板过程的塑性变形,得到不同喷射角度与等效塑性应变沿真实路径距离的关系,并通过拉伸试验进行验证。喷射角度为90°的强化研磨加工伸长率为1.4%,相比未经过强化研磨加工的伸长率数值缩减了2.0%。断口收缩率由空白组的4.9%降低到喷射角为90°的2.2%。结合仿真和试验可知,强化研磨加工中喷射角度越大,塑性变形能力越低,材料加工越难。     

Preparation of ZrC/SiC porous self-supporting monoliths via sol-gel process using polyethylene glycol as phase separation inducer

We present a straightforward method via sol-gel process using polyethylene glycol (PEG) as phase separation inducer to prepare zirconium carbide/silicon carbide (ZrC/SiC) porous monoliths. Organic/inorganic hybrid gels are prepared using zirconium oxychloride, furfuryl alcohol, and tetraethyl orthosilicate as major starting materials. In the presence of PEG, crack-free hybrid monoliths are obtained by drying the wet gels under ambient pressure, whereas in the absence of PEG, the wet gels break into pieces as expected. PEG plays a key role in maintaining the macroscopic shape of the monoliths. After ceramization at 1300–1500?°C, ZrC/SiC porous monoliths are obtained. SEM and mercury intrusion porosimetry data show that PEG also has strong influence on the microstructures of the monoliths. The compressive strengths of the ceramic monoliths are in the range of 0.3 to 0.7?MPa. And their compressive behavior starts to differ due to the changes in their microstructures, especially the pore structure.